High Temperature Ceramic Putty - (SavesPast HTCP)
Offer Price :
USD $ 67.77 / Kg USD $ 56.57* / Kg
( * Inclusive of all taxes and freight )
High Temperature Ceramic Putty
Rebuilding putty for tough wear and high temperature resistance till 230°C
A two component paste general purpose ceramic-filled epoxy system based on high temperature resistance special resin .The ceramic putty is used to repair high wear areas against sliding abrasion /erosion of processing equipment's , interfacing metallic, low-friction surfaces and extends wear life for high temperature service conditions. Ideally used for scrubbers, cyclones, dust collectors, and fan housings. The high temperature putty requires post-curing for proper performance and temperature resistance.

Product Specification Details

PROPERTIES
STANDARD
UNIT
VALUES
Pack Size
1 Kg
Coverage
-
cm2/pack size/thickness
624 Cm2 / kg / 5 mm
Color and Apperance
ASTM D 1544
-
Grey & Thick paste
Specific Gravity
ASTM D 1475-98
-
1.94
Mix Ratio By Weight
Manual
-
13.1(R):1(H)
Mix Ratio By Volume
Manual
-
6(R):1(H)
Pot Life @ 30°C
IS 101
min
120
Functional Cure
ASTM D 1640
Hrs
16
Compressive Strength
ASTMD 695
N/mm2
71
More info  

Features of High Temperature Ceramic Putty

  • Fast,cost effective and durable
  • High compressive strength and extreme chemical resistance
  • Good resistance to corrosion and abrasion
  • Efficient alternate method of repair where welding or brazing would be undesirable or impossible
  • Can Repair Intricate shape or forms/thin sections, difficult to weld metals
  • No equipment/Power supply needed
  • Unlimited cycle of repairs
  • Less Labor costs - Avoid assembly/disassembly, Pre Machining/Post Machining
  • Resistant to chemicals and most acids, bases, solvents, and alkalis
  • Superior adhesion – forms a solid bond to steel, cast iron,
  • Stainless steel, concrete, and clean and abraded bronze, copper, and aluminum.
  • Eliminates costly wear part inventory
  • No shrinkage, expansion or distortion
  • Excellent electrical insulation characteristics
  • Can do repairs at In-situ repair, In-Plant, Workshops, Remote areas
  • No VOC's
  • Routine Maintenance and Unexpected Maintenance
  • Repair cost at fraction of replacement cost

Where to Use?

  • Fixing wear resistant moulds
  • Cyclone and separator bodies
  • Dust collectors and exhausters
  • Fan blades and housings
  • Intake manifolds